Chemical Composition
|
Element |
Composition Limits, % |
|||
|
UNS N06002 |
UNS N06230 |
UNS N12160 |
UNS R30556 |
|
|
Nickel |
remainderA |
remainderA |
remainderA |
19.0-22.5 |
|
Iron |
17.0-20.0 |
3.0 max |
3.5 max |
remainderA |
|
Chromium |
20.5-23.0 |
20.0-24.0 |
26.0 30.0 |
21.0-23.0 |
|
Cobalt |
0.5-2.5 |
5.0 max |
27.0-33.0 |
16.0-21.0 |
|
Molybdenum |
8.0-10.0 |
1.0-3.00 |
1.0 max |
2.5-4.0 |
|
Tungsten |
0.2-1.0 |
13.0-15.0 |
1.0 max |
2.0-3.5 |
|
Carbon |
0.05-0.15 |
0.05-0.15 |
0.15 max |
0.05-0.15 |
|
Silicon |
1.00 max |
0.25-0.75 |
2.4 3.0 |
0.20-0.80 |
|
Manganese |
1.00 max |
0.30-1.00 |
1.5 max |
0.50-2.00 |
|
Phosphorus |
0.04 |
0.030 max |
0.030 max |
0.04 max |
|
Sulfur |
0.03 |
0.015 max |
0.015 max |
0.015 max |
|
Columbium |
... |
... |
1.0 max |
0.30 max |
|
Tantalum |
... |
... |
... |
0.30-1.25 |
|
Aluminum |
... |
0.50 max |
... |
0.10-0.50 |
|
Zirconium |
... |
... |
... |
0.001-0.10 |
|
Lanthanum |
... |
0.005--0.050 |
... |
0.005-0.10 |
|
Nrogen |
... |
... |
... |
0.10-0.30 |
|
Boron |
... |
0.015 max |
... |
0.02 max |
|
Titanium |
... |
... |
0.20-0.80 |
... |
Note:
A. Chemical Analysis—Test Methods E 1473. For elements not covered by Test Methods E 1473, the referee method shall be as agreed upon between the manufacturer and the purchaser. The composition of the remainder element shall be determined arithmetically by difference.
Mechanical Properties
|
UNS |
Tensile Strength, min, ksi (MPA) |
Yield Strength (0.2 % Offset), min, ksi (MPa) |
Elongation in 2 in. (50.8mm) or 4DA min, % |
|
N06002 |
95 (660) |
35 (240) |
35 |
|
N06230B |
110 (760) |
45 (310) |
40 |
|
N12160C |
90 (620) |
35 (240) |
40 |
|
R30556D |
100 (690) |
45 (310) |
40 |
Note:
A. D refers to the diameter of the tension specimen.
B. Solution annealed at a temperature between 2200 to 2275°F (1204 to 1246°C) followed by a water quench or rapidly cooled by other means.
C. Solution annealed at 1950°F (1065°C) minimum.
D. Solution annealed at 2100°F (1150°C) minimum.